Azs Refractory Spouts, Tubes, Orifice Rings, Plungers for Glass Furnace Gob Feeder Machines

• Customization: Available
• Material: Zircon
• Refractoriness (℃): 1580< Refractoriness< 1770
• Shape: Block
• Usage: Glass Manufacturing
• Zirconium Content: Zirconium Content<30%
• Delivery Time: 30days
• Samples: Free Samples
• New Product: Total New
• Color: White
• Transport Package: Wooden Crate
• Specification: ZR 15%min
• Trademark: GTN
• Origin: China
• Production Capacity: 2000pieces Per Month

Product Description

Description  of the goods	Apparent porosity	Bulk density≥	Apparentporosity≤	refractoriness under load	Refractorinessunder load(0.2MPa)	Thermal shock stability (1100 ºC, in cold water)
Orifice ring	g/ cm3	%	MPa	°C	ºC
	22.5	2.07	18	1320	1650	18 times min

The Physical and Chemical Indicators 

Zr33# material physical and chemical indicators
Material		Zr28% puritry
Chemical Component(%)	AL2O3	≥65
	ZrO2	≥19
	SIO2	≤15
	Fe2O3	≤0.1
Apparent porosity		≤17
Density		≥3.0
Pressure resistance strength		≥110Mpa
RUL		≥1700

How can make the Sillimanite orifice ring?

 

The raw material has Sillimanite 0.5-3mm 30-40%, 0.088-0.5mm 20-30%,<0.088mm 20-30%, clay 8-12%, sulfite pulp waste liquid 3%, all the material mixed in a mixer. According to the mud ratio, add particle materials for dry mixing for 1 minute,  add binder for mixing for 3 minutes, and then add fine powder for mixing for 4-6 minutes. The mud moisture is controlled in 3-3.5%. The embryo is formed under 14.7MPA,  and dry for 3-4 days at 40-60 ºC, and fire at 1450 ºC.

We are the professional factory in producing different kinds of refractory materials for glass industry.Any question, you can contact us without hesitation.

What is the glass furnace/kiln orifice ring and how many different material of orifice ring we have?

 

Orifice ring is widely used in glass furnace/kiln as the feeder when the glass is melt forming. Orifice ring takes the most important role in control of the molten glass flow speed.

It has good thermal stability,resistance to glass liquid erosion,low pollution to glass liquid, which is a common refractory material for IS Machine in all over the world. There are single drop, double drop, three drop, four drop, six drop and we also can make them as customers' own drawings.

Orifice ring can pass the glass liquid in the glass liquid pool of the furnace to the glass processing equipment, such as glass blowing machines. It is necessary to choose different raw material orifice ring according to the glass furnace temperature and the character of the glass liquid material.

We have four differenty types orifice ring according to the different raw material, they are sillimanite,Zirconium33, Quartz and Corundum mullite. Customers can choose different types according to the furnace types, glass output, glass tpyes. We can make the orifice ring Customization. Because it will take 1-2 hours to change the orifice ring, good quality orifice ring can make the production continuous work.